直拉SiGe合金的高温Seebeck系数
Seebeck Coefficient of Czochralski SiGe Alloy at High Temperatures
摘要 为了更好地发掘SiGe合金的热电转换性能的潜力,对几组不同的SiGe合金样品进行了性能测试,主要是对不同参数样品的Seebeck系数值进行对比,从而得出热电性能的最佳组合.不仅比较了不同组分、不同晶向和不同导电类型样品的Seebeck系数,还对单晶SiGe合金和多晶SiGe合金的热电性能进行了对比分析.发现SiGe合金的Seebeck系数具有明显的各向异性,(100)晶向的Seebeck系数明显优于(111》晶向.Seebeck系数与测试温度具有非常密切的依赖关系,随着温度的变化所有样品均在700~900K的温度范围内出现了峰值.此外还对SiGe合金的Seebeck系数与组分的关系进行了详细描述.
Abstract:
To investigate the possibility of improvement in the thermoelectric properties of SiGe alloys, we examined several different silicon-germanium alloys with different contents,orientations,and electric conductive types. The thermoelectric properties of single crystal SiGe alloy were compared with those of poly-crystals. Experiment results show that the Seebeck coefficient of the sample depends on the temperature. All the samples show a maximal Seebeck coefficient in the temperature range of 700~900K. The Seebeck coefficient of the sample with (111) orientation is smaller than that of the sample with <100> orientation at the same temperature. The Seebeck coefficient of the SiGe alloy also depends on Ge content.
Author: Suo Kainan Zhang Weilian Niu Xinhuan Jiang Zhongwei
作者单位: 河北工业大学半导体材料研究所,天津,300130 河北工业大学微电子技术研究所,天津,300130
刊 名 半导体学报 ISTICEIPKU
年,卷(期): 2007, 28(z1)
分类号: TN377
机标分类号: TH1 TH2
在线出版日期: 2008年1月7日
基金项目: 河北省自然科学基金